Mig Welder Choice 110 or 220

I've always preferred 220 over 110. Once you learn how to weld you can do anything with a 220. It's not so much the machine as it is technique. 220 will allow you to tackle the thicker stuff that the 110 will require more passes. Practice on scrap first to get the machine dialed in then remember to disperse your spot welds over a large area to give it time to cool so you don't warp the chit out of your panels. Plenty of us on this forum that are willing to give you pointers, or at least I am so don't hesitate to ask. But I would go 220