Well, it's cracked. How bad is it?
That crack isn't going to travel any (especially into the thicker block metal) since there is no stress on it, but a loose section of the metal around it could come loose later just from heat cycle.
I also have to disagree on the need to smooth anything, but just get any possible loose bits off.