Block crack

That's a high stress area, but at least you don't have oil to worry about. I'm not sure if it's a candidate for pinning. Grinding out the cracks, preheating then welding with high nickel rod, followed by a slow cool. With the head bolt hole there, it would have to be re-tapped. Might be easier to find another flathead.